[China Glass Net] Liquor glass bottles are often seen in our lives. There are many styles, not only transparent bottles, but also a frosted bottle. Many friends are very curious about the frosted wine bottle, so I really want to know what the frosting technology is. To help you understand this aspect, we will introduce it in detail below. The frosting is on the glass of the product, and the glass glaze powder of a certain size is adhered. After baking at a high temperature of 580~600 °C, the glass glaze coating is melted on the surface of the glass and is displayed with a different color from the glass body. A decorative method. Adhesive glass glaze powder, can be brushed with a pen, or can be rolled with a rubber roller. Through the silk screen processing, the floor pattern of the frosted surface can be obtained. The method comprises: silk-screening a pattern pattern formed by a flux-blocking agent on the surface of the glass article. After the pattern pattern to be printed is air-dried, it is subjected to frosting. Then, after high-temperature baking, the frosted surface without the pattern pattern is melted on the glass surface, and the place where the silk screen pattern is applied is not melted on the glass surface due to the action of the flux inhibitor. After baking, the transparent floor pattern appears through the translucent sand surface, forming a special decorative effect. Frosted silk screen printing resistant consists of ferric oxide, talc, clay, etc., ground with a ball mill, with a fineness of 350 mesh, and blended with a binder before silk screen printing. 1. Ingredients, according to the designed material list, weigh the various raw materials and mix them evenly in a mixing machine. The main raw materials of glass are: quartz sand, limestone, feldspar, soda ash, boric acid and the like. 2. Melting, the prepared raw materials are heated at a high temperature to form a uniform bubble-free glass liquid. This is a very complicated physical and chemical reaction process. The melting of the glass takes place in the furnace. There are two main types of melting furnaces: one is a kiln, and the glass is contained in the crucible and heated outside the crucible. The small kiln has only one raft, and the big one can have up to 20 rafts. The kiln is produced by gap type, and now only optical glass and color glass are produced in the kiln. The other is a pool kiln in which the frit is melted and the open flame is heated on the upper side of the glass. The melting temperature of glass is mostly between 1300 and 1600 ゚C. Most of them are heated by flame, and a small amount is heated by electric current, which is called electric melting furnace. Now, the pool kiln is continuously produced. The small pool kiln can be several meters, and the large one can be as large as 400 meters. 3. Forming is to convert the molten glass into a solid product having a fixed shape. Forming must be carried out within a certain temperature range. This is a cooling process in which the glass first changes from a viscous liquid state to a plastic state and then to a brittle solid state. The forming method can be divided into two major categories: manual forming and mechanical forming. Shangri-la curtains are using polyester fiber fabrics, not easy to edge grinding, environmentally friendly. Strong shading, simple structure of the track and bracket in the installation of more convenient, and easy to clean, long time bright as new fabric. Shangri-la curtain can be divided into pearl chain pull type and electric take-away type according to the operation mode, which can not only reduce the solar radiation, but also keep the indoor air smooth. White Roller Blinds,Fabric Window Shades,Shades Window Blinds,Curtain Blind Shangri-La SHAOXING JEVA IMP.&EXP CO., LTD. , https://www.xhcurtain.com